• Primerless to glass
• 3 Hour Minimum Drive Away Time (MDAT); tested according to FMVSS 212
• Can be used for non-conductive applications
• Short cut-off string

Sikaflex® P2G has been specifically designed for the Automotive Glass Replacement business. It is ideal for mobile and in-shop installations. This product is to be used by professional, experienced users only. Related process information in this PDS is specifically for Automotive Glass Replacement. For other applications, tests with actual substrates and conditions have to be performed to ensure adhesion and material compatibility.

SPECIFICATIONS:
Chemical base: 1 Component Polyurethane
Color (CQP001-1):Black
Cure Mechanism: Moisture-Curing
Non-sag properties: Excellent
Application temperature: Product 10 – 35 °C (50 – 95 °F), Ambient 4 – 43 °C (40 – 110 °F), Substrate 4 – 54 °C (40 – 130 °F)
Skin time (CQP019-1):30 minutes
Open time (CQP526-1):15 minutes
Tensile strength (CQP036-1 / ISO 527):5 MPa (750 psi)
Elongation at break (CQP036-1 / ISO 527):400 %
Tensile lap-shear strength (CQP046-1 / ISO 4587):3 MPa (400 psi)
Service temperature (CQP509-1 / CQP513-1):-40 – 93 °C (-40 – 200 °F)
CQP = Corporate Quality Procedure: A) 23 °C (73 °F) / 50 % r.h. B) Stored below 25 °C (77 °F)

APPLICATION LIMITS:

Avoid contact with alcohol and alcohol containing solvents during cure.
Do not apply over silicones or in the presence of curing silicones.
Glass parts must always be installed within the open time.  The open time is significantly shorter in hot and humid climates.  Never install any glass part after the product has built a skin.