• For High Performance Glazing of Large Lites of Glass Exceeding 100 United Inches* Without the Need for Spacer Shims
• 100% Solids Content
• Accommodates High Windloading Even at Elevated Temperatures
• Black Color

CRL 100+ Load Bearing Butyl Architectural Glazing Tape is made from a blend of rubber polymers. It is designed for glazing large lites of glass exceeding 100"* without the need for spacer shims. 100+ Tape transfers high wind loads evenly, from the glass to the window frame, and will accommodate high wind loading at elevated temperatures. It enables the project to be glazed from the inside. The 100 percent solids content formula will not shrink or absorb moisture, but will compress to accommodate variances in pocket width. It comes on release paper rolls and is positioned for quick alignment during installation. Application temperature range is 20° to 120° (-7° to 49°C), and life expectancy if properly applied is 20 years.

APPLICABLE STANDARDS: AAMA 804.3, 806.3, and 807.3, ASTM C1281.

TYPICAL PROPERTIES:
Base Polymer: butyl rubber (polyisobutylene)
Solids Content: 100% solids (no asbestos).
Cure Time: Fully cured before application.
Hardness: 20 durometer Shore "A" @ 77° (25°C).
Temperature Range: Application 20°F (-7°C) to 120° (49°C); Service -40°F (-40°C) to 190°F (88°C).
VOC Content: 0%. Joint Movement: ±15% of joint width.
Service Life: 20 year minimum.l cap bead (such as silicone) to prevent over compression or use CRL 100+ Load Bearing Glazing Tape.

Product Warning:

NOTE: United Inches = width + height